Effects of Firing Conditions on the Coal Ash Fusibility Test

Abstract

In the present work, the melting behaviour of ashes obtained from the combustion of coals from different seams were investigated by a laboratory-scale equipment. The ash melting behaviour was studied by heating the specimens in a tubular furnace under a controlled gas atmosphere, while continuous monitoring the shape transformation by a digital camera. The ash fusibility temperatures (AFT) were determined by using an application which allows the in-line identification of the AFTrelated shapes specified in the ASTM D 1857-04.
The effect of the furnace gas-atmosphere on the determination of the ash fusion temperatures were studied by performing the measurements under dry-air, SO₂-rich-air and humidified air environments. It was found that under dry conditions, AFT determination is significantly affected by slag foaming, leading to an overestimation of the melting temperatures. Low water vapour concentrations does not appreciably change the results obtained under dry air, while SO₂-rich atmosphere seems to reduce foaming. As a result, since no volume expansion was observed, samples heated under SO₂-air flow, apparently melt at lower temperatures with respect to dry air conditions. The mineral phases transformation of the ashes during the heating process was studied by X-Ray diffraction and it was found that the low temperature transformations are essentially related to Iron and Alkalis reaction with aluminosilicates to form a glassy phase. On the other hand, high temperatures transformations are related to quartz and mullite solubilization which is closely dependent to the amount of Calcium, and therefore of anorthite phase, in the ash sample.